Corrosion Resistance: Excellent resistance to various corrosive environments,
including sulfuric acid, phosphoric acid, and seawater.
Pitting and Crevice Corrosion Resistance: High resistance due to the
combination of chromium, molybdenum, and nitrogen.
Weldability: Good weldability with no need for post-weld heat treatment.
Tensile Strength: Minimum 700 MPa (101,500 psi).
Yield Strength: Minimum 350 MPa (50,750 psi).
Elongation: Minimum 35%.
Hardness (Brinell): Approximately 220 HB.
Chemical Processing: Ideal for handling sulfuric, phosphoric, and nitric
acids.
Oil & Gas Industry: Used in sour gas wells, pipelines, and other
corrosive environments.
Desalination Plants: Resists chloride-induced corrosion.
Pollution Control Equipment: Resists corrosion in flue gas
desulfurization units.
Pharmaceutical and Food Industries: Suitable for processing equipment
due to its corrosion resistance.
Thickness: 3mm to 100mm (depending on the requirement).
Width: 1000mm to 2500mm.
Length: 2000mm to 6000mm.
Surface Finish: Mill finish, pickled, and passivated.
Standards: ASTM B625, ASME SB625, DIN 1.4562.
Types: Elbows, Tees, Reducers, Caps, Stub Ends, Couplings, etc.
Size Range: 1/8" to 48" (varies based on type).
Pressure Rating: 150# to 2500#.
Connection Type: Welded, seamless, threaded, flanged.
Standards: ASTM B366, ASME SB366, DIN 1.4562.
Modulus of Elasticity: ~200 GPa.
Impact Strength: High impact strength, even at low temperatures.
Thermal Conductivity: Low thermal conductivity compared to other alloys.
Density: 8.10 g/cm³.
Standards: ASTM B625, ASTM B366, NACE MR0175/ISO 15156.
Certification: Mill Test Certificate (MTC) as per EN 10204 3.1/3.2,
Third-Party Inspection, ISO 9001.
| Parameter | Specification |
|---|---|
| Material Composition | Nickel (Ni) ~31%, Chromium (Cr) ~26-27%, Molybdenum (Mo) ~6.5%, Iron (Fe) Balance, Nitrogen (N) ~0.2%, Copper (Cu) ~1.2%, Manganese (Mn) ~2%, Silicon (Si) ~0.3%, Carbon (C) ~0.015% |
| Corrosion Resistance | Excellent in sulfuric acid, phosphoric acid, seawater, and various other corrosive environments |
| Pitting and Crevice Resistance | High resistance due to Cr, Mo, and N combination |
| Weldability | Good; no post-weld heat treatment required |
| Tensile Strength | Minimum 700 MPa (101,500 psi) |
| Yield Strength | Minimum 350 MPa (50,750 psi) |
| Elongation | Minimum 35% |
| Hardness (Brinell) | Approximately 220 HB |
| Impact Strength | High, even at low temperatures |
| Modulus of Elasticity | ~200 GPa |
| Density | 8.10 g/cm³ |
| Thermal Conductivity | Low compared to other alloys |
| Service Temperature Range | -196°C to +400°C |
| Parameter | Specification |
|---|---|
| Thickness | 3mm to 100mm |
| Width | 1000mm to 2500mm |
| Length | 2000mm to 6000mm |
| Surface Finish | Mill finish, pickled, passivated |
| Standards | ASTM B625, ASME SB625, DIN 1.4562 |
| Parameter | Specification |
|---|---|
| Types | Elbows, Tees, Reducers, Caps, Stub Ends, Couplings, etc. |
| Size Range | 1/8" to 48" |
| Pressure Rating | 150# to 2500# |
| Connection Type | Welded, seamless, threaded, flanged |
| Standards | ASTM B366, ASME SB366, DIN 1.4562 |